Carbon Fiber Filled PTFE Tube Rod Sheet

Basic Info

Model NO.	Rptfe rod sheet tube
Warranty	2 Years
Material	PTFE
Water Absorption	0.1%~0.3%
Contraction Percentage	＜0.4%
Colour	Black, Brown, White
Certificate	ISO9001-2000, Fad, RoHS, SGS
Outside Dia	1~1200mm
Thickness	0.2~500mm
Apparent Density	2.10~2.30g/cm3
Temperature	-180~+260 Degree
Tensile Strength(Min)	18MPa
Crack Elongation(Min)	230%
Productivity	100 Tons /Month
MOQ	50kgs
Transport Package	Exported Wooden Case Outside, Plastic Film Inside
Specification	GB
Trademark	Senrong
Origin	Zibo, Shandong, China
HS Code	39172900
Production Capacity	100tons /Month

Product Description

(1)made of PTFE resin and a certain filling agent such as carbon fiber, graphite, molybdenum disulfide, glass fiber and bronze powder.

(2)PTFE filling products are made of high-speed mixing PTFE resin and a certain volume of filling agent such as carbon fiber, graphite, molybdenum disulfide, glass fiber and bronze powder etc., shaped by moulding, then through high heat sintering. We can also produce according to clients' requests.

(3)it is homogeneous in structure with smooth surface, not permitting the crack, air bubble, separated layer, mechanical damage and so on.

Because of the addition of filling agent, some characteristics of PTFE are greatly improved, especially for the abrasion resistance, heat conduction, contravariance and self-lubrication, which are obviously better than pure PTFE products. It is suitable to be used in the temperature range of -180-+260 as sealing parts or guiding parts.

Changed characters by filling chemical substance:

Glass fiber: Increases compressive strength, rigidity and wear. Reduces creep and cold flow

Minimal effect on chemical and electrical properties

Carbon: Increases compressive strength, hardness, wear, and load properties. Good chemical resistance. Various types and amounts of carbon can be added to alter conductivity

Bronze: Increases hardness and wear resistance. Increases dimensional stability and compressive strength. Not suitable for corrosive or electrical applications

Molybdenum disulfide: Increases hardness, stiffness, and wear. Minimal effect on chemical and electrical properties

Graphite: Reduces coefficient of friction. Reduces initial wear. Increases strength.

Properties	Unit	Result
Apparent density	g/cm ³	2.10-2.30
Tensile strength(min)	Mpa	18
Crack elongation (min)	%	230